Keperluan kimia
|
Elemen
|
Komposisi, %
|
|||||||
|
Jenis 1
|
Jenis 1b
|
Jenis 2
|
Jenis 2b
|
Jenis 3
|
Jenis 4
|
Jenis 5
|
Jenis 6
|
|
|
Karbon, Jumlah, Max
|
3.00 | 3.00 | 3.00 | 2.60 | 2.60 | 2.40 | 2.40 | 3.00 |
|
Silikon
|
1.00-2.80 | 1.00-2.80 | 1.00-2.80 | 1.00-2.80 | 1.00-2.00 | 5.00-6.00 | 1.00-2.00 | 1.50-2.50 |
|
Mangan
|
0.5-1.5 | 0.5-1.5 | 0.5-1.5 | 0.5-1.5 | 0.5-1.5 | 0.5-1.5 | 0.5-1.5 | 0.5-1.5 |
|
Nikel
|
13.50-17.50 | 13.50-17.50 | 18.00-22.00 | 18.00-22.00 | 28.00-32.00 | 29.00-32.00 | 34.00-36.00 | 18.00-22.00 |
|
Tembaga
|
5.50-7.50 | 5.50-7.50 | 0.50max | 0.50max | 0.50max | 0.50max | 0.50max | 3.50-5.50 |
|
Chromium
|
1.5-2.5 | 2.50-3.50 | 1.5-2.5 | 3.00-6.00A | 2.50-3.50 | 4.50-5.50 | 0.10max | 1.00-2.00 |
|
Sulfur, Max
|
0.12 | 0.12 | 0.12 | 0.12 | 0.12 | 0.12 | 0.12 | 0.12 |
|
Molybdenum, Max
|
... | ... | ... | ... | ... | ... | ... | 1.00 |
ADi mana beberapa pemesinan diperlukan, julat kromium 3.00-4.00 % disyorkan.
Keperluan mekanikal
|
Jenis 1
|
Jenis 1b
|
Jenis 2
|
Jenis 2b
|
Jenis 3
|
Jenis 4
|
Jenis 5
|
Jenis 6
|
|
|
Kekuatan tegangan, min, ksi (MPA)
|
25(172) | 30(207) | 25(172) | 30(207) | 25(172) | 25(172) | 20(138) | 25(172) |
|
Kekerasan Brinell (3000 kg)
|
131 183 | 149 212 | 118 174 | 171 248 | 118 159 | 149 212 | 99 124 | 124 174 |
|
Dimensi
|
Saiz blok "Y"
|
|||||
|
Untuk casting ketebalan kurang
daripada 1/2 inci (13 mm)
|
Untuk casting ketebalan 1/2 in.
(13 mm) ke 1 1 / 2 in. (38 mm)
|
Untuk casting ketebalan
1 1 / 2 in. (38 mm) dan lebih
|
||||
|
dalam.
|
mm |
dalam.
|
mm |
dalam.
|
mm | |
| A |
1⁄2
|
13 | 1 | 25 | 3 | 75 |
| B | 1 5/8 | 40 | 2 1/8 | 54 | 5 | 125 |
| C | 2 | 50 | 3 | 75 | 4 | 100 |
| D | 4 | 100 | 6 | 150 | 8 | 200 |
| E | 7 | 175 | 7 | 175 | 7 | 175 |
|
lebih kurang
|
lebih kurang
|
lebih kurang
|
lebih kurang
|
lebih kurang
|
lebih kurang
|
|
Nota1-1 /16 dalam .=1.6 mm; 1/8 dalam .=3.2 mm.